Evaluación de actividad fungicida de nanopartículas de cobre y manganeso sobre Fusarium spp, causante de enfermedades fitopatógenas en cultivos de banano
| dc.contributor.advisor | Cruzat Contreras, Christian Américo | |
| dc.contributor.author | Gómez Siranaula, Mateo Fernando | |
| dc.date.accessioned | 2025-08-27T20:33:01Z | |
| dc.date.available | 2025-08-27T20:33:01Z | |
| dc.date.issued | 2025-08-26 | |
| dc.description | Las nanopartículas (NPs) han emergido como una alternativa innovadora para el manejo sostenible de enfermedades fitopatógenas. En este estudio se evaluó la actividad biocida de nanopartículas de cobre y manganeso frente a cepas de Fusarium spp. in vitro, sintetizadas mediante el método solvotermal en un reactor de acero inoxidable. Las NPs de cobre se obtuvieron a 180 °C durante 18 horas, mientras que las de manganeso se sintetizaron a 100 °C con tiempos de 12 y 16 horas, empleando como precursores nitrato cúprico pentahidratado y acetato de manganeso (II) tetrahidratado. La actividad antifúngica se analizó mediante el método de difusión en agar, registrando el crecimiento micelial a los 7, 14 y 21 días. Los resultados mostraron que las NPs de cobre sintetizadas con acetona presentaron efecto fungistático, mientras que las obtenidas con PEG exhibieron actividad fungicida a 2000 ppm contra Fusarium spp.. El análisis de microscopía de fuerza atómica (AFM) reveló tamaños promedio de 110,40 nm (acetona) y 48,64 nm (PEG) para las NPs de cobre, y de 15,54 nm (12 h) y 28,62 nm (16 h) para las de manganeso. Por su parte, la espectroscopía UV-Visible confirmó la presencia de NPs con máximos de absorción en 329 nm (cobre) y 216 nm (manganeso). Estos resultados demuestran el potencial de las nanopartículas metálicas como agentes antifúngicos para el control de enfermedades agrícolas. | |
| dc.description.abstract | Nanoparticles (NPs) have emerged as an innovative alternative for the sustainable management of phytopathogenic diseases. In this study, the biocidal activity of copper and manganese nanoparticles against Fusarium spp. strains was evaluated in vitro, with synthesis carried out through the solvothermal method using a stainless-steel reactor. Copper NPs were obtained at 180 °C for 18 hours, while manganese NPs were synthesized at 100 °C for 12 and 16 hours, using copper (II) nitrate pentahydrate and manganese (II) acetate tetrahydrate as precursors. Antifungal activity was assessed by the agar well diffusion method, recording mycelial growth at 7, 14, and 21 days. The results showed that copper NPs synthesized with acetone exhibited fungistatic effects, whereas those obtained with PEG demonstrated fungicidal activity at 2000 ppm against Fusarium spp.. Atomic force microscopy (AFM) analysis revealed average sizes of 110.40 nm (acetone) and 48.64 nm (PEG) for copper NPs, and 15.54 nm (12 h) and 28.62 nm (16 h) for manganese NPs. Additionally, UV-Visible spectroscopy confirmed the presence of nanoparticles with absorption peaks at 329 nm (copper) and 216 nm (manganese). These findings highlight the potential of metallic nanoparticles as antifungal agents for the control of agricultural diseases. | |
| dc.description.uri | 0000-0002-4373-1407 | |
| dc.format | application/pdf | |
| dc.format.extent | 50 páginas | |
| dc.identifier.uri | https://dspace.ucuenca.edu.ec/handle/123456789/47171 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad de Cuenca | |
| dc.relation.ispartof | TBQ; 931 | |
| dc.rights | https://creativecommons.org/licenses/by-nd/4.0 | |
| dc.rights.accessRights | openAccess | |
| dc.subject | Bioquímica | |
| dc.subject | Solvotermal | |
| dc.subject | Nanotecnología | |
| dc.subject | Biocontrol agrícola | |
| dc.subject | Espectroscopía ultravioleta | |
| dc.subject.other | Bioquímica::Compuestos Químicos | |
| dc.title | Evaluación de actividad fungicida de nanopartículas de cobre y manganeso sobre Fusarium spp, causante de enfermedades fitopatógenas en cultivos de banano | |
| dc.type | bachelorThesis | |
| dcterms.description | Bioquímico Farmacéutico | |
| dcterms.spatial | Cuenca, Ecuador |