Efecto del espesor y material Cad/Cam en la resistencia a la fatiga de molares tratados endodónticamente restaurados con carillas oclusales
| dc.contributor.advisor | Delgado Gaete, Bolívar Andrés | |
| dc.contributor.author | Salto Ortiz, David Gustavo | |
| dc.date | 2027-06-16 | |
| dc.date.accessioned | 2025-06-18T14:56:29Z | |
| dc.date.available | 2027-06-17 | |
| dc.date.available | 2025-06-18T14:56:29Z | |
| dc.date.issued | 2025-06-18 | |
| dc.description | Los dientes tratados con endodoncia pierden una cantidad de tejido dental sano al realizar las preparaciones, los cuales deben cumplir con los espesores indicados por el fabricante para garantizar la resistencia del material. Objetivo general: Evaluar la influencia del grosor y tipo de material sobre la resistencia a la fractura en dientes tratados con endodoncia (ETT) restaurados con carillas oclusales (OV). Materiales y métodos: Se incluyeron 60 órganos dentales extraídos con fines de ortodoncia o periodontales, los cuáles se dividieron en grupo control, grupo Cerasmart 0,5-0,6mm, grupo Cerasmart 1,5-1,6mm, grupo Celtraduo 0,5- 0,6mm y grupo Celtraduo 1,5-1,6mm. Los grupos experimentales se prepararon de acuerdo a los espesores mencionados. Se realizó una prueba de Kruskal-Wallis; para los datos post hoc se realizó la prueba T3 de Dunnett. Resultados: El grupo experimental que presentó el valor más alto fue el G. CeltraDuo 1,5-1,6mm con 618,21 newton, seguido del Cerasmart 1,5- 1,6mm con 579,14 newton. Entre los grupos control y CeltraDuo 0,5-0,6mm hubo una diferencia significativa p=0.025. Conclusión: La evaluación del grosor de la restauración reveló que un mayor grosor no influye en la resistencia a la fractura de los premolares tratados con endodoncia. | |
| dc.description.abstract | Endodontically treated teeth lose a certain amount of healthy dental tissue to make the preparations, which must comply with the thicknesses indicated by the manufacturer to guarantee their resistance. General Objective: To evaluate the influence of the thickness and type of material on fracture resistance in endodontically treated teeth (ETT) restored with occlusal veneers (OV). Materials and methods: 60 dental organs extracted by orthodontics or periodontics were included and divided into control group, Cerasmart 0.5-0.6mm group, Cerasmart 1.5-1.6mm group, Celtraduo 0.5-0.6mm group and Celtraduo 1.5-1.6mm group. The experimental groups were prepared according to the aforementioned thicknesses. A Kruskal-Wallis test was performed, for post hoc data the T3 Dunnett test was performed. Results: The experimental group that presented the highest value was G. CeltraDuo 1.5- 1.6mm with 618.21 newton, followed by Cerasmart 1.5-1.6mm with 579.14 newton. Between the control and CeltraDuo 0.5-0.6mm groups there was a significant difference p=0.025. Conclusion: Evaluation of restoration thickness revealed that increased restoration thickness does not influence the fracture resistance of endodontically treated premolars. | |
| dc.description.uri | 0000-0001-5586-2829 | |
| dc.format | application/pdf | |
| dc.format.extent | 68 páginas | |
| dc.identifier.uri | https://dspace.ucuenca.edu.ec/handle/123456789/46966 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad de Cuenca | |
| dc.relation.ispartof | TE4-ODONRO; 036 | |
| dc.rights | https://creativecommons.org/licenses/by-nc-sa/4.0 | |
| dc.rights.accessRights | openAccess | |
| dc.subject | Odontología | |
| dc.subject | Carilla oclusal | |
| dc.subject | Restauración dental | |
| dc.subject | Cad/Cam | |
| dc.subject.other | Odontología::Rehabilitación oral | |
| dc.title | Efecto del espesor y material Cad/Cam en la resistencia a la fatiga de molares tratados endodónticamente restaurados con carillas oclusales | |
| dc.title.alternative | EFECTO DEL ESPESOR Y MATERIAL CAD/CAM EN LA RESISTENCIA A LA FATIGA DE MOLARES TRATADOS ENDODÓNTICAMENTE RESTAURADOS CON CARILLAS OCLUSALES | |
| dc.type | masterThesis | |
| dcterms.description | Especialista en Rehabilitación Oral y Prótesis Implanto Asistida | |
| dcterms.spatial | Cuenca, Ecuador |