Diseño y evaluación de mezclas de cemento polimérico como material alternativo para la fabricación de instrumentos musicales
Loading...
Date
2024-11-27
Journal Title
Journal ISSN
Volume Title
Publisher
Universidad de Cuenca
Abstract
This undergraduate thesis presents a study on the viability of using polymer concrete
as an alternative material to wood in the manufacture of musical instruments. Mixtures of Portland cement and epoxy resin were designed and evaluated in various
proportions, with their mechanical properties analyzed: compressive strength, flexural
strength, density, and elasticity percentage. The results indicate that the 1:1 (cement-
resin) mixture provides acceptable properties, with a compressive strength of 25.35
MPa, a flexural strength of 13.8 MPa, a density of 1.46 g/cm3, and an elasticity
percentage of 1.76%. Using this mixture, a prototype musical instrument (electric
bass guitar) was manufactured, demonstrating its structural viability as an alternative
to traditional materials
Resumen
Este trabajo de titulación presenta un estudio sobre la viabilidad de utilizar cemento
polimérico como material alternativo a la madera en la fabricación de instrumentos
musicales. Se diseñaron y evaluaron mezclas de cemento Portland y resina epóxica en
diferentes proporciones y se analizó sus propiedades mecánicas: resistencia a la
compresión, resistencia a la flexión, densidad y porcentaje de elasticidad. Los resultados
muestran que la mezcla 1:1 (cemento-resina) ofrece propiedades aceptables, con una
resistencia a la compresión de 25.35 MPa, una resistencia a la flexión de 13.8 MPa, una
densidad de 1.46 g/cm3 y un porcentaje de elasticidad del 1.76%. Con esta mezcla se
fabricó un prototipo de instrumento musical (Bajo Eléctrico), demostrando su viabilidad
estructural como alternativa a los materiales tradicionales