Publication: Syndiotactic poly (propene-co-norbornene): synthesis and properties at low norbornene incorporation
Loading...
Date
2010
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
Copolymerizations of propene with norbornene were carried out using a syndiotactic metallocene catalyst at low initial comonomer concentrations for different polymerization times. The influence of the norbornene concentration on the catalytic activity and on the resulting material properties has been analyzed. The copolymer molecular weight decreased drastically when small amounts of norbornene were added in reactions which lasted 30 min. When longer reaction times were used the molecular weight increased with time, however living polymerizationwas ruled out because the polydispersity was ca. 2. The DSC measurements showed copolymers with low crystallinity or which were completely amorphous.
Description
Las copolimerizaciones de propeno con norborneno se llevaron a cabo utilizando un catalizador metaloceno sindiotáctico a bajas concentraciones iniciales de comonómero para diferentes tiempos de polimerización. Se ha analizado la influencia de la concentración de norborneno en la actividad catalítica y en las propiedades del material resultante. El peso molecular del copolímero disminuyó drásticamente cuando se añadieron pequeñas cantidades de norborneno en reacciones que duraron 30 min. Cuando se utilizaron tiempos de reacción más largos, el peso molecular aumentó con el tiempo, sin embargo, se descartó la polimerización viva porque la polidispersidad era de aprox. 2. Las mediciones de DSC mostraron copolímeros con baja cristalinidad o completamente amorfos.
Keywords
Poly (Propene-Co-Norbornene), Syndiotactic metallocene, Thermal properties