Publication: Syndiotactic polypropylene copolymer membranes and their performance for oxygen separation
Loading...
Date
2010
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
Syndiotactic poly(propylene- -olefin) copolymers with controlled microstructure and desired properties for oxygen enrichment have been synthesized via metallocene catalysts. The controlled incorporation of comonomers as pendant branch mainly improved the oxygen permeability, but the oxygen/nitrogen selectivity dropped around 20%. By controlling the amount and length of the branches in the syndiotactic polypropylene, the permeability of the membrane was enhanced up to 12-fold and it is comparable to typical commercial polymers used for this application. In contrast with conventional commercial polypropylene, copolymers with a large amount of comonomer were soluble in cyclohexane, allowing the manufacture of composite membranes with high permeance.
Description
Se sintetizaron copolímeros sindiotácticos de poli (propileno-olefina) con microestructura controlada y propiedades deseadas para el enriquecimiento de oxígeno a través de catalizadores metaloceno. La incorporación controlada de comonómeros como ramificación mejoró principalmente la permeabilidad al oxígeno, pero la selectividad de oxígeno / nitrógeno descendió alrededor del 20%. Al controlar la cantidad y la longitud de la ramificación en el polipropileno sindiotáctico, la permeabilidad de la membrana mejoró hasta 12 veces y es comparable a los polímeros comerciales típicos utilizados para esta aplicación. A diferencia del polipropileno comercial convencional, los copolímeros con una gran cantidad de comonómero fueron solubles en ciclohexano, lo que permite la fabricación de membranas compuestas con alta permeabilidad.
Keywords
Syndiotactic polypropylene, Polyolefin membranes, Gas separation, Oxygen enrichment, Composite membranes