Title: | Análisis de peso estructural de resina de impresión Onx SprintRay para prótesis fija plural |
Other Titles: | ANÁLISIS DE PESO ESTRUCTURAL DE RESINA DE IMPRESIÓN ONX SPRINTRAY PARA PRÓTESIS FIJA PLURAL |
Authors: | Lupú Flores, Billy Darlin Pacurucu Mendieta, Miguel David |
metadata.dc.contributor.advisor: | Abad Coronel, Cristian Gustavo |
metadata.dc.description.uri: | 0000-0002-5326-681x |
metadata.dc.subject.other: | CIUC::Medicina::Odontología::Rehabilitación Oral |
Keywords: | Odontología Resina impresa Peso estructural Prótesis plural fija |
Issue Date: | 3-Oct-2023 |
metadata.dc.format.extent: | 22 páginas |
Publisher: | Universidad de Cuenca |
metadata.dc.type: | bachelorThesis |
Abstract: | El objetivo del presente estudio es proveer evidencia científica sobre el análisis del peso
estructural de una prótesis fija plural de un material polimérico obtenida por técnica aditiva
(3DPP), con la finalidad de ofrecer una alternativa viable para el tratamiento de prótesis fija
plural e implantes dentales. Métodos. Se trabajó a partir de una estructura de resina impresa
3D de 4 piezas dentales que van desde las piezas 2.3 a 2.6, dicha estructura se sometió a
fuerzas compresivas que simularon el sistema masticatorio del ser humano por medio de un
equipo de ensayo universal, se realizó un análisis de elementos finitos 3D, para determinar
la deformidad del material. Resultados. La masa de la estructura fue de 1,98 gr, en los
ensayos de fuerzas compresivas soportó una carga de 1000,88 N, su distribución de tensión
fue de 16,726 MPa; mientras que su fuerza tensional fue 143,916 MPa. En el análisis de
elementos finitos de la estructura 3DPP realizado en el software Ansys, se observó una
deformación con un valor de 0,001mm, y distribución de tensión del material de 15,36 MPa.
En valores de estrés se registró un valor mínimo de 2533,4 MPa y un de máximo 12667 MPa.
Conclusiones. Se determinó el peso estructural del material 3DPP, aportando información
importante para tomar en consideración en la utilización de PPF, comprobando así la
funcionalidad y desempeño de la misma. |
Description: | The objective of this study is to provide scientific evidence on the analysis of the structural
weight of a plural fixed prosthesis of a polymeric material obtained by the additive technique
(3DPP), in order to offer a viable alternative for the treatment of plural fixed prostheses and
dental implants. Methods. We worked from a 3D printed resin structure of 4 dental pieces
ranging from pieces 2.3 to 2.6, said structure was subjected to compressive forces that
simulated the masticatory system of the human being by means of a universal test equipment,
a 3D finite element analysis was carried out to determine the deformity of the material. Results.
The mass of the structure was 1.98 gr, in the compressive force tests it supported a load of
1000.88 N, its stress distribution was 16.726 MPa; while its tensile strength was 143,916 MPa.
In the finite element analysis of the 3DPP structure carried out in the Ansys software, a
deformation with a value of 0.001mm was observed, and a stress distribution of the material
of 15.36 MPa. In stress values, a minimum value of 2533.4 MPa and a maximum value of
12667 MPa were recorded. Conclusions. The structural weight of the 3DPP material was
determined, providing important information to take into consideration in the use of PPF, thus
verifying its functionality and performance. |