Abad Salinas, Yulissa RaquelArmijos Freire, Sandra Daniela2025-06-042027-04-222025-06-042025-06-04https://dspace.ucuenca.edu.ec/handle/123456789/46944Antecedentes: La restauración de dientes tratados endodónticamente ha sido un desafío para los odontólogos. Objetivo: Determinar el efecto del composite reforzado con fibras cortas y con fibras de polietileno sobre la resistencia a la fractura en premolares endodónticamente tratados. Métodos: Se realizó un estudio de cohorte in vitro con 40 premolares superiores, de los cuales 10 conformaron el grupo control (G4). Treinta dientes fueron sometidos a endodoncia, preparaciones cavitarias estandarizadas y se dividieron en tres grupos restaurativos: (G1) fibras de polietileno Ribbond con resina compuesta fluida, (G2) fibras de polietileno Ribbond más composite reforzado con fibras cortas (everX posterior), y (G3) únicamente composite reforzado con fibras cortas (everX posterior), con 10 dientes en cada grupo. Se aplicó una carga de compresión oblicua (30°) hasta la fractura. Resultados: Los resultados muestran que los premolares intactos (grupo control, G4) presentaron la mayor resistencia a la fractura con un promedio de 440,710 ± 28,147 N. Entre los grupos experimentales, el grupo fibra Ribbond + everX Posterior (G2) obtuvo la mayor resistencia (330,710 ± 27,475 N), seguido por el grupo everX Posterior (G3) con 257,934 ± 57,124 N. Las diferencias entre los grupos restaurados fueron estadísticamente significativas (P < 0.05). La distribución de Weibull reflejó que el grupo G2 presentó la mayor confiabilidad (m = 11.644). Conclusión: La combinación de fibra Ribbond con everX Posterior (G2) mostró la mayor resistencia, mientras que la fibra Ribbond sola (G1) obtuvo la más baja.Background: Previous studies have shown that endodontically treated teeth are at critically higher risk of fracture compared to vital teeth because tissue loss compromises the structural strength of the endodontically treated tooth. Objective: To determine the effect of short fiberreinforced composite and polyethylene fibers on fracture resistance in endodontically treated premolars, period 2023-2024. Methods: An in vitro cohort study was conducted with 40 maxillary premolars, of which 10 formed the control group (G4). Thirty teeth underwent endodontic treatment, standardized cavity preparations, and were divided into three restorative groups: (G1) Ribbond polyethylene fibers with flowable composite resin, (G2) Ribbond polyethylene fibers plus short fiber-reinforced composite, and (G3) only short fiberreinforced composite, with 10 teeth in each group. An oblique compressive load (30°) was applied until fracture. Results: Results show that intact premolars (control group, G4) showed the highest fracture resistance with an average of 440,710 ± 28,147 N. Among the experimental groups, the Ribbond fiber + everX Posterior group (G2) obtained the highest resistance (330,710 ± 27,475 N), followed by the everX Posterior group (G3) with 257,934 ± 57,124 N. The differences between the restored groups were statistically significant (P < 0.05), indicating a consistent variation in fracture resistance depending on the material used. The Weibull distribution reflected that group G2 presented the highest reliability (m = 11.644). Conclusion: The combination of Ribbond fiber with everX Posterior (G2) showed the highest strength, while Ribbond fiber alone (G1) had the lowest.application/pdf40 páginasspahttps://creativecommons.org/licenses/by-nc-sa/4.0OdontologíaResistencia flexionalEndodonciaResinas compuestasOdontología::EndodonciamasterThesisopenAccess