Pinos Vélez, Verónica PatriciaLoayza Cueva, Camila Maite2025-09-052025-09-052025-09-04https://dspace.ucuenca.edu.ec/handle/123456789/47256En este trabajo se evalúa la decoloración de aguas residuales provenientes del teñido artesanal de paja toquilla a través de procesos de fotocatálisis y foto-Fenton, utilizando como catalizador ferrita de zinc sintetizada a partir de reactivos comerciales y de pilas alcalinas. Se prepararon y caracterizaron las ferritas, evaluando su estructura, área superficial y porosidad, observándose que la ferrita de pilas posee menor área superficial, pero poros más amplios, lo que influye en su actividad catalítica. Los experimentos con fotocatálisis arrojaron remociones del colorante anilina roja menores a un 2%, mientras que con el proceso foto- Fenton se alcanzaron remociones de un 33.4% para ferrita de reactivos comerciales y de un 40.2% para ferrita de pilas en 3 horas. El análisis estadístico mediante ANOVA y la prueba post hoc encontraron diferencias estadísticamente significativas entre los porcentajes de decoloración alcanzados con el método foto-Fenton, pero para la fotocatálisis no se encontraron diferencias estadísticamente significativas por tipo de ferrita. El estudio cinético reveló que la degradación sigue un modelo de pseudo primer orden con constante cinética promedio de 0.003 min-1, y el diseño factorial 2 2 evidenció que tanto la cantidad de catalizador como la dosis de H2O2 afectan la eficiencia. Estos resultados permitieron identificar que el tratamiento más eficiente es el de foto-Fenton con ferrita obtenida de pilas alcalinas, afirmando que esta ferrita es viable como un catalizador para el tratamiento de aguas residuales.This work evaluates the decolorization of wastewater from artisanal toquilla straw dyeing through photocatalysis and photo-Fenton processes, using zinc ferrite synthesized from commercial reagents and alkaline batteries as catalysts. The ferrites were prepared and characterized by assessing their structure, surface area, and porosity. It was observed that the battery-derived ferrite has a lower surface area but larger pores, which influences its catalytic activity. Photocatalysis experiments resulted in removals of the aniline red dye below 2%, whereas the photo-Fenton process achieved removals of 33.4% for ferrite from commercial reagents and 40.2% for battery-derived ferrite within 3 hours. Statistical analysis using ANOVA and post hoc tests found statistically significant differences between the decolorization percentages achieved with the photo-Fenton method, but no significant differences were observed by ferrite type in photocatalysis. The kinetic study revealed that the degradation follows a pseudo-first order model with an average rate constant of 0.003 min-1 and a 22 factorial design showed that both the catalyst amount and H2O2 dosage affect the efficiency. These results identified the most efficient treatment as the photo-Fenton process using ferrite obtained from alkaline batteries, confirming that this ferrite is a viable catalyst for wastewater treatment.application/pdf56 páginasspahttps://creativecommons.org/licenses/by-nd/4.0Ingeniería QuímicaFoto-fentonFerrita de zincDecoloraciónBioquímica::Compuestos QuímicosbachelorThesisopenAccess